Black Liquid Silicone Encapsulants Potting Compound Gel For LED / Solar Cells

RTV2 Addition Cure Silicone Potting Compound

Description

Black Liquid Silicone Encapsulants Potting Compound Gel For LED/Solar Cells/Circuits Electronic Potting

Silicone compound is supplied as a two-component addition cure system. It consists of Part A and Part B. The component A is white and component B is black for easy identification and inspection of complete mixing.(colors can be adjusted as per customer requirement.) When the components are thoroughly mixed in a 1:1 ratio by weight or volume, the liquid mixture cures to a flexible elastomer, which is suited for electrical/electronic potting and encapsulating applications.

Applications

Silicone is a general purpose compound suited for adhesive and coating. This cost-effective silicone can be used in a variety of electronic potting applications including the adhesive and coating for solar power, HID, LCD displayers, circuit board and electronic components, etc.

Features

Silicone compound has a excellent electrical property features in resistant to temperature, corrosion, radiation, insulation, waterproof, damp proofing, shock resistance, thermal conducting, inflaming retarding and weather ability, etc. It can be long-term used under -50℃～200℃.

Typical properties

Item No.: RTV160A/B

Appearance(A/B) White/Grey liquid

Viscosity(A/B,Mpa.s) 3700±2000

Mix ratio (A/B) 1:1

Pot life after curing(25℃,min) 30-40

Curing time (hrs) 2-4

Thermal conductivity(W/m·K)(A/B) ≥0.60

Durometer Hardness(JIS A⁰) 56

Volume resistivity(Ω·cm) 7X10¹⁴

Dielectric breakdown voltage(KV/mm) ≥20

Flammability classification UL-94 V-0

Shrinkage % 0.01

Using Instructions

Silicone compound part A and Part B should be thoroughly mixed at a 1:1 ratio (weight or volume) before using. Pour into the electronic components after vacuum de-airing. Silicone compound may be cured at room temperature or accelerated with heat.

Precautions

• The curing time varies due to different temperature, the higher temperature, it cures faster. Users can adjust the ratio of catalyst according to the temperature in order to get an ideal curing speed.
• Certain materials can inhibit the cure of Silicone rubber. The most notable include: sulfur, polysulfide, sulfur-containing material, Organ tin and organ metallic compound, etc.
• Prevent from contact with tin, phosphorus, water, ammonium, chlorine, carboxylic acid, hydroxyl compound, etc. to avoid un-curing circumstance.

Packing and Storage

• Silicone rubber is shipped as kits that Part A and B liquid components in separate containers. It is available in packing in 5kg or 20kg,200kg per pail.
• Silicone rubber must be tightly sealed in cool and dry place, prevented from sun and rain. Transport by non-dangerous goods.